Metalworking Hunttalkers!

[Redmt]

You got my curiosity up as to what I have on hand.
I have a 25# Ranomatic D that says it runs any polarity and is flux core.
#25 lincore 60-0
#10 Postalloy 2832 says Either polarity with any gas.
I guess I'm running out of excuses except it's boring.

 

[millerkiller77]

You got my curiosity up as to what I have on hand.
I have a 25# Ranomatic D that says it runs any polarity and is flux core.
#25 lincore 60-0
#10 Postalloy 2832 says Either polarity with any gas.
I guess I'm running out of excuses except it's boring.

If they are out of the sealed plastic bag just laying around the shop for years and years, they may give you some troubles dialing in

 

[Redmt]

If they are out of the sealed plastic bag just laying around the shop for years and years, they may give you some troubles dialing in

I have a good size cabinet for rod and wire. I also use sealed rod containers for open cans of rod. I weld too big a variety of crap so I have 3 shitloads of different fillers. There's nothing worse than setting up for a weld with funky consumables. First hand experience unfortunately.

 

[np307]

Funny yall should mention flux core, I burned a fair bit of it today making this forklift barrier. A departure from our normal work but still pays the bills. A little wavy but it won't be noticeable after a week or so.

 

[millerkiller77]

Funny yall should mention flux core, I burned a fair bit of it today making this forklift barrier. A departure from our normal work but still pays the bills. A little wavy but it won't be noticeable after a week or so. View attachment 267708

Visual barrier or really small forklift?

 

[np307]

Visual barrier or really small forklift?

Just to keep them from stacking pallets against the building.

 

[220yotekiller]

MIG I could do a lot of welds without looking

l do a lot of my mig where l can't see it, under fittings and whatnot.

 

[millerkiller77]

My son just started an arc welding course at the local community College. He's really enjoying it as a filler to break up the boredom with his normal courses. To be fair though, he's already been mig welding and using plasma since he was 10 so he has a bit more knowledge than a newbie. These are some of his daily trinkets he brings home..

 

[Redmt]

Nice . I take it those were root passes? It would be interesting to see a cut and etch.

 

[Hem]

And here i sit, nothing but blobs with 6010.

 

[Redmt]

And here i sit, nothing but blobs with 6010.

Start with an easier to run rod. 7014 can make you look like a pro. 6013 is also a shallow penetration "butter rod" . I have always preferred 6011 to 6010. 6011 is pretty forgiving.

 

[Hem]

Start with an easier to run rod. 7014 can make you look like a pro. 6013 is also a shallow penetration "butter rod" . I have always preferred 6011 to 6010. 6011 is pretty forgiving.

7018 had me feeling pretty psyched, but the 6010 shamed me.
Looking forward to trying MIG.

 

[Redmt]

7018 had me feeling pretty psyched, but the 6010 shamed me.
Looking forward to trying MIG.

The problem with mig is the weld can look beautiful with almost zero structural value. Just as you think you have mig nailed, run an open root vertical up and the fillets vertical down. When you nailed vertical, see how your open root overhead comes out. Practice practice practice

 

[np307]

A little 6010 and a lot of 7018 to burn today.

 

[np307]

First plant shutdown I've worked. 12 hours of prefab yesterday, call time of 0500 today. We're rolling along. This is a heat exchanger swap for a CIP system at a food plant.

 

[GoGriz]

This thread pushed me to finally give welding a try. I borrowed a buzz box from a family member and used an angle grinder for all my cuts and grinding. It was a rough start and the welds look terrible, but they only need to hold about 300 lbs for the project so I think it should ok (hopefully). I’m glad I finally took the plunge!

 

[Redmt]

This thread pushed me to finally give welding a try. I borrowed a buzz box from a family member and used an angle grinder for all my cuts and grinding. It was a rough start and the welds look terrible, but they only need to hold about 300 lbs for the project so I think it should ok (hopefully). I’m glad I finally took the plunge!

View attachment 269138

I will very respectfully say "no comment". I think that next time practice on something you don't want.

 

[Sytes]

It's all good for a first. It's all about the puddle and the heat. Pushing or pulling. What's it for? 300#'s? I dig it! We all start somewhere and that's not bad for a first crack at it! It's a fun as all heck hobby!

 

[GoGriz]

I know it’s really thought, but for a few hours of work I’m just happy I didn’t light anything on fire. I’ll keep practicing and refining things moving forward (I might grind most of the welds out and lay them down again at some point). I am building a 20’ tall tripod tower to drop a 250’ weight from, for a testing project.

 

[np307]

First plant shutdown I've worked. 12 hours of prefab yesterday, call time of 0500 today. We're rolling along. This is a heat exchanger swap for a CIP system at a food plant. View attachment 268984View attachment 268985View attachment 268986View attachment 268987View attachment 268988

Started at 0500, ended at 0030. I fit and welded most of this section after my post yesterday: